Sangyinary 发表于 20-11-26 19:48:49

LC竞速卡差速接杯淬火

2S电池跑了10组电池，原厂接杯磨损有3mm深的口子。听大家说原厂接杯没有经过热处理所以太软，买了新的直接燃气炉加热水淬，希望会好一些…不知道论坛大神没有没有其他更好的办法https://app.rcfans.com/public/emotion/face_032.png
http://image.rcfans.com/pic/20201126/1606391220616911_291.jpg?x-oss-process=image/watermark,image_cGljLzIwMjAwNzIxL29zc18xNTk1MzM4ODExNTY2XzIzMl8xMThfMzI2LnBuZw==,t_50,g_se,x_20,y_20
http://image.rcfans.com/pic/20201126/1606391220697207_426.jpg?x-oss-process=image/watermark,image_cGljLzIwMjAwNzIxL29zc18xNTk1MzM4ODExNTY2XzIzMl8xMThfMzI2LnBuZw==,t_50,g_se,x_20,y_20
http://image.rcfans.com/pic/20201126/1606391220906550_530.jpg?x-oss-process=image/watermark,image_cGljLzIwMjAwNzIxL29zc18xNTk1MzM4ODExNTY2XzIzMl8xMThfMzI2LnBuZw==,t_50,g_se,x_20,y_20
http://image.rcfans.com/pic/20201126/1606391221115245_101.jpg?x-oss-process=image/watermark,image_cGljLzIwMjAwNzIxL29zc18xNTk1MzM4ODExNTY2XzIzMl8xMThfMzI2LnBuZw==,t_50,g_se,x_20,y_20
http://image.rcfans.com/pic/20201126/1606391221298113_451.jpg?x-oss-process=image/watermark,image_cGljLzIwMjAwNzIxL29zc18xNTk1MzM4ODExNTY2XzIzMl8xMThfMzI2LnBuZw==,t_50,g_se,x_20,y_20

行侠仗义懒洋洋 发表于 20-11-26 20:13:24

真的会变结实吗 ，我以为只有个别金属淬火后回硬

快使用双截棍 发表于 20-11-26 21:12:20

瞎搞，搞不好还不如之前呢https://app.rcfans.com/public/emotion/face_009.png

somin123456 发表于 20-11-26 21:20:31

听说有用，用油冷却一下

GLOBE 发表于 20-11-26 22:35:17

不是放水里，要放油里，慢慢冷却

ttkk 发表于 20-11-27 01:03:28

草原雄鹰丹东1 发表于 20-11-27 06:39:55

这不是退火吗？会变软吗？

remote2wd 发表于 20-11-27 18:17:08

温度掌握好了很有用，我的整完之后用3s跑了十组左右都没肉眼可见的磨损

Sangyinary 发表于 20-11-27 20:33:50

somin123456 发表于 2020-11-26 21:20
听说有用，用油冷却一下

一般降温越快越容易形成马氏体，大件因为怕表面降温太快内应力增加才用降温慢的油淬吧～

Sangyinary 发表于 20-11-27 20:35:31

remote2wd 发表于 2020-11-27 18:17
温度掌握好了很有用，我的整完之后用3s跑了十组左右都没肉眼可见的磨损

镀镍层有剥落么，烧红了直接水淬镀镍层会剥落呢https://app.rcfans.com/public/emotion/face_032.png